Evaluation of six different one-step universal adhesive systems in terms of dentin bond strength, adhesive interface characterization, surface tension, contact angle, degree of conversion and solvent evaporation after immediate and delayed use


Journal of Esthetic and Restorative Dentistry, vol.35, no.3, pp.479-492, 2023 (SCI-Expanded) identifier identifier identifier

  • Publication Type: Article / Article
  • Volume: 35 Issue: 3
  • Publication Date: 2023
  • Doi Number: 10.1111/jerd.12973
  • Journal Name: Journal of Esthetic and Restorative Dentistry
  • Journal Indexes: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, CINAHL, EMBASE, MEDLINE
  • Page Numbers: pp.479-492
  • Keywords: bond strength, contact angle, delayed bonding, solvent evaporation, surface tension, universal adhesive, HYBRID LAYER, ENAMEL
  • Kayseri University Affiliated: No


© 2022 Wiley Periodicals LLC.Objectives: In this study, it was aimed to investigate the effects of different waiting periods on resin-dentin bond strength (BS), degree of conversion (DC), contact angle (CA), surface tension (ST), solvent evaporation (weight loss) and the characteristics of adhesive interfaces of the current six universal adhesive resins (ARs). Materials and Methods: A total of 216 caries-free human lower third molar teeth were used. Composite resin restorations were performed by applying six universal ARs in etch-and-rinse and self-etch mode on standardized dentin surfaces after 0, 5, and 30 min waiting time. Then, a micro-shear BS test, SEM examination and characterization of the adhesive interface were performed. In addition, DC, CA, ST, solvent evaporation of all tested ARs were evaluated. Results: The obtained data were statistically anaIyzed. The tested ARs did not show any statistical difference between 0 and 5 min evaluations in all parameters evaluated except for weight loss (p > 0.05). While the weight loss, ST and CA of all ARs increased in 30 min (p < 0.05), the BS, DC, thickness of the adhesive layer and the hybrid layer, resin tag length and number of resin tags varied according to the ARs used. When the ARs were used in etch-and-rinse mode, all the parameters evaluated also varied according to the AR used. Higher adhesive layer thickness and lower hybrid layer thickness were found in the self-etch mode (p < 0.05). Conclusions: All of the adhesives tested can be safely used up to 30 min. This could also prevent economical loss caused by waste adhesive material. Clinical Significance: It is important to know how the bond strength, degree of conversion, adhesion, contact angle and surface tension properties of the adhesive resin waiting in the dispensing cup for a long time during clinical use are affected to make ideal restorations.