Journal of Craniofacial Surgery, cilt.33, sa.1, ss.41-47, 2022 (SCI-Expanded)
Copyright # 2021 by Mutaz B. Habal, MDPurpose: To evaluate the effects of 2 different surface roughness values produced by sandblasted, large-grit, and acid-etched treatments at different loading conditions on the stability of mini-screws. Material and Methods: A total of 56 mini-screws (Group 1; 28 with Ra value of 1 mm, Group 2; 28 with Ra value of 1.5 mm) were inserted into the tibia of fourteen New Zealand rabbits. Surface analysis was performed before the placement of the miniscrews using multi-technique characterization. The mini-screws were loaded with 500 grf after different healing times: unloaded, immediate, 4 and 8 weeks. Resonance frequency analyses were performed immediately after mini-screw placement and at the end of loading. Biomechanical and histomorphometric analyses were also performed at the end of the loading period. Results: All mini-screws preserved their stability at the end of the loading period. However, the resonance frequency analyses showed higher implant stability quotient scores for 8-week group, unlike the immediate loading and unloaded groups (P < 0.05). According to the infinite focus microscopy results, prolongation of healing time resulted in a greater bone area on the loaded mini-screws in Group 2 (P < 0.05). Similarly, the histomorphometric analysis revealed higher bone-to-implant contact values in the 8-week group. There was no significant difference in the stability between the miniscrews with the Ra values of 1 and 1.5 mm. Conclusions: Sandblasted, large-grit, and acid-etched treated miniscrews showed significantly higher stability with healing time under heavy forces. Sandblasted, large-grit, and acid-etched treated miniscrews can be removed without fracture of the screw or the bone surfaces.